品名
|
AWS型号
|
熔敷金属化学成分(%)
|
熔敷金属力学性能
|
特征与用途
|
|
C
|
Si
|
Mn
|
P
|
S
|
Ni
|
Cr
|
Mo
|
Cu
|
σ0.2(MPa)
|
δb(MPa)
|
δ(%)
|
Akv(J)
|
|
DW-308
|
E308T0-1/4
|
0.05
|
0.57
|
1.52
|
0.020
|
0.009
|
9.68
|
19.72
|
0.02
|
0.03
|
390
|
570
|
41
|
0℃:39
|
用于平焊和横角焊，适于焊接SUS304钢
|
|
DW-308L
|
E308LT0-1/4
|
0.027
|
0.56
|
1.49
|
0.019
|
0.008
|
10.02
|
19.53
|
0.02
|
0.03
|
370
|
550
|
42
|
0℃:41
|
适于焊接SUS304L钢,用于平焊和横角焊,与DW-308相比,DW-308L含碳量较低
|
|
DW-308LP
|
E308LT1-1/4
|
0.027
|
0.55
|
1.51
|
0.022
|
0.010
|
9.89
|
19.45
|
0.02
|
0.03
|
380
|
550
|
45
|
0℃:57
|
用于对接焊和角焊，适于全位置焊，与DW-308相比，DW-308LP的含碳量较低，适于焊接SUS304和SUS304L钢
|
|
DW-309
|
E309T0-1/4
|
0.035
|
0.58
|
1.22
|
0.021
|
0.009
|
12.48
|
24.03
|
0.03
|
0.02
|
450
|
590
|
32
|
0℃:33
|
用于不锈钢与其它钢的异种钢焊接和复合钢过渡层焊接
|
|
DW-309L
|
E309LT0-1/4
|
0.028
|
0.61
|
1.24
|
0.019
|
0.010
|
12.58
|
24.17
|
0.05
|
0.03
|
450
|
580
|
33
|
|
用于不锈钢与其它钢的异种钢焊接和复合钢过渡层焊接与DW-309相比DW-309L的含碳量较低
|
|
DW-309MoL
|
E309LmoT0-1/4
|
0.027
|
0.61
|
1.18
|
0.019
|
0.009
|
12.60
|
23.20
|
2.37
|
0.03
|
540
|
720
|
30
|
|
用于不锈钢与其它钢的异种钢焊接和复合钢过渡层焊接
|
|
DW-316L
|
E316LT0-1/4
|
0.026
|
0.59
|
1.43
|
0.020
|
0.010
|
12.02
|
18.95
|
2.54
|
0.06
|
380
|
540
|
41
|
0℃:44
|
适用于焊接SUS316L钢，用于平焊和横角焊，与DW-316相比，DW-316L的含碳量较低
|
|
DW-308H
|
E308HT1-1/4
|
0.060
|
0.42
|
1.50
|
0.02
|
0.007
|
9.62
|
18.68
|
|
|
370
|
560
|
48
|
0℃:71
|
用于焊接高温下使用的18%Cr-8%Ni不锈钢
|
|
DW-309LH
|
E309LT1-1/4
|
0.029
|
0.41
|
1.25
|
0.021
|
0.008
|
12.61
|
23.79
|
|
|
380
|
590
|
36
|
|
用于不锈钢与其它钢的异种钢焊接和复合钢过渡层焊接
|
|
DW-316H
|
E316T1-1/4
|
0.050
|
0.38
|
1.10
|
0.019
|
0.006
|
11.60
|
18.75
|
2.40
|
|
390
|
570
|
41
|
0℃:68
|
用于焊接高温下使用的18%Cr-12%Ni-2%Mo不锈钢
|
|
DW-316LH
|
E316LT1-1/4
|
0.023
|
0.45
|
1.08
|
0.020
|
0.007
|
11.94
|
18.47
|
2.45
|
|
390
|
540
|
44
|
0℃:66
|
用于焊接高温热处理的18%Cr-12%Ni-2%Mo不锈钢
|
|
DW-308LT
|
E308LT0-1/4
|
0.026
|
0.45
|
237
|
0.023
|
0.009
|
10.30
|
18.60
|
|
|
380
|
530
|
51
|
-196℃:39
|
用于焊接低温下使用的18%Cr-8%Ni不锈钢
|