<table class="ke-zeroborder" width="95%" align="center" border="0"> <tbody> <tr> <td align="right" width="60%"><span class="JQ">D707</span></td> <td style="padding-left:1em;vertical-align:middle;" width="40%">符合 GB EDW-A-15<br /> </td> </tr> <tr> <td colspan="2"> <p><br /> <strong>说明:</strong> 采用碳钢为焊芯的低氢钠型药皮碳化钨堆焊焊条，依靠药皮中碳化物合金过渡，堆焊金属含钨量80-85%，由于药皮较厚，合金元素多，可交直流焊接接，使用适当的电流堆焊。</p> </td> </tr> <tr> <td colspan="2"> <p><br /> <strong>用途:</strong> 用于堆焊耐岩石强烈磨损之机械零件，如混凝土搅拌机叶片、推土机和泵浦叶片、挖泥机叶片、高速混砂箱 机械设备等。</p> </td> </tr> <tr> <td class="Metal" colspan="2"><strong><br /> 熔敷金属化学成分(%)</strong> <table class="ke-zeroborder" bordercolor="#d4d0c8" cellspacing="1" width="100%" bgcolor="#000000" border="0"> <tbody> <tr bgcolor="#cccccc"> <td height="20"> <div align="center">化学成分 </div> </td> <td height="20"> <div align="center">C</div> </td> <td height="20"> <div align="center">Mn</div> </td> <td height="20"> <div align="center">Si</div> </td> <td height="20"> <div align="center">W</div> </td> </tr> <tr bgcolor="#ffffff"> <td> <div align="center">保证值</div> </td> <td> <div align="center">1.50~3.00</div> </td> <td> <div align="center">≤2.00</div> </td> <td> <div align="center">≤4.00</div> </td> <td> <div align="center">80.0~85.0</div> </td> </tr> </tbody> </table> </td> </tr> <tr> <td colspan="2"><strong><br /> </strong><strong>堆焊层硬度:</strong> HRC≥85</td> </tr> <tr> <td colspan="2"><strong><br /> </strong><strong>参考电流</strong> (DC+) <table class="ke-zeroborder" bordercolor="#d4d0c8" cellspacing="1" width="100%" bgcolor="#000000" border="0"> <tbody> <tr bgcolor="#cccccc"> <td height="20"> <div align="center">焊条直径(mm) </div> </td> <td valign="bottom" height="20"> <div align="center">φ3.2</div> </td> <td valign="bottom" height="20"> <div align="center">φ4.0</div> </td> <td valign="bottom" height="20"> <div align="center">φ5.0</div> </td> </tr> <tr bgcolor="#ffffff"> <td> <div align="center">焊接电流(A) </div> </td> <td> <div align="center">70~120</div> </td> <td> <div align="center">140~180</div> </td> <td> <div align="center">180~220</div> </td> </tr> </tbody> </table> </td> </tr> <tr> <td valign="top" colspan="2"><br /> <strong>注意事项</strong>:<br /> 1.焊前焊条须经300-350℃烘焙1h。<br /> 2.堆焊件为碳钢时预热温度在300℃以上，堆焊件为低合金钢时预热温度为400-500℃，堆焊件为不锈钢时预热温度为600-650℃。<br /> 3.低合金钢及不锈钢焊后须经700℃退火。<br /> </td> </tr> </tbody> </table>